LNP™ LUBRICOMP™ RAL22S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BQbNSP_LNPLUBRICOMPRAL22Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RAL22S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound RAL-4022 HS Product reorder name: RAL22S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.9 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 81.4 | MPa | ASTM D638 |
| Fracture | 79.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 8.1 | % | ASTM D638 |
| Fracture | 9.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2960 | MPa | ASTM D790 |
| -- | 3500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 110 | MPa | ASTM D790 |
| -- | 117 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.55 | ASTM D3702 Modified | |
| With Self-Static | 0.46 | ASTM D3702 Modified | |
| Wear Factor - Washer | 13.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 750 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.00 | J | ASTM D3763 |
| -- | 1.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 249 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 198 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 193 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB2061 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| BESTNYL SE30VI01AT | Triesa Plastics | Nylon 66 | BESTNYL |
| FRAGOM PR/900 ELAS | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Hangzhou Jinxin VMPET Packaging Film | Hangzhou Jinxin Filming Packaging Co., Ltd. | Film, PET | Hangzhou Jinxin |
| Hostacom X M3 T14 C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |