LAPEROS® A150
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | LAPEROS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BQ2WaX_LAPEROS-A150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard, Glass fiber reinforced, High stiffness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.81 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 1.00 mm | 0.40 | % | |
| Flow : 1.00 mm | 0.11 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 180 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 20500 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Flexural Strain | 1.8 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | VF2001/BK210P |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 44 | kV/mm | |
| 3.00 mm | 28 | kV/mm | |
| Dielectric Constant | IEC 60250 | ||
| 1 kHz | 4.50 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 kHz | 0.020 | ||
| 1 MHz | 0.020 | ||
| Arc Resistance | 180 | sec | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1 mm; Inj. Pressure 60MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant PBT PBT-1100 | Clariant Corporation | PBT | Clariant PBT |
| DynaPath™ C1410CF | Polymer Dynamix | PBT | DynaPath™ |
| HIDEN® C100 | YUHWA Korea Petrochemical Ind. Co., Ltd. | CPE | HIDEN® |
| INSTRUC PA612GF20 | Infinity LTL Engineered Compounds | Nylon 6/12 | INSTRUC |
| Plenco 06500 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |