Abstron SE-32M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bhansali Engineering Polymers Limited |
| Trademark: | Abstron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BPMdhk_Abstron-SE-32M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Abstron SE-32M is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by sheet extrusion molding and is available in the Asia-Pacific region. The application fields of Abstron SE-32M include thin plates, automobile industry and consumer goods. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 43.1 | MPa | ASTM D638 |
| Flexural Modulus (6.40 mm) | 2010 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 63.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.20 mm | 440 | J/m | ASTM D256 |
| 6.40 mm | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 3.0 - 3.5 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Cylinder Zone 1 Temp. | 220 - 235 | °C | |
| Melt Temperature | 220 - 240 | °C | |
| Die Temperature | 215 - 235 | °C |
| Extrusion instructions |
|---|
| Drying Time (Tray Oven): 3 to 3.5 hrDrying Time (Hopper Dryers): 2.5 to 3 hrDrying Time (Dry Air Ovens): 2 to 2.5 hrVacuum: >600 mm HgRoller Temperature - Down Stack Top: 95°CRoller Temperature - Down Stack Middle: 80°CRoller Temperature - Down Stack Bottom: 90°CRoller Temperature - Up Stack Top: 95°CRoller Temperature - Up Stack Middle: 85°CRoller Temperature - Up Stack Bottom: 95°C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® QA200N | Solvay Specialty Polymers | PPS | Ryton® |
| Chemlon® 235G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Ferro PP LPP30BC92GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Estane® 58213 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Sylvin 8687-55 Green 3159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |