Kumho ABS HU601
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Korea Kumho Petrochemical Co., Ltd. |
| Trademark: | Kumho ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BOl693_Kumho-ABS-HU601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Features: Odorless, Heat resistance Applications: Automobile parts demanding for heat resistance and odorless |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/21.6 kg | 9.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.80 | % | ASTM D955 |
| -- | 0.50 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 49.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 20 | % | ASTM D638 |
| Break | 24 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2060 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 69.0 | MPa | ISO 178 |
| Yield | 63.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 240 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 180 | J/m | ASTM D256 |
| 23°C | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 106 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1360 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Nanjing Hongrui PA66 A1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Hifax TYC 1123P RXF Black | LyondellBasell Industries | TPO (POE) | Hifax |
| Jiangsu Sinarise JM8011 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| ESTOPLAST XU 430BL16 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |