| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BOYAsU_Kynar-740.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR® 740 is a semi-crystalline medium-high molecular weight pelletized polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties which qualify it for high performance service in a wide range of applications. It is a thermoplastic fluoropolymer capable of being fabricated in standard processing equipment. The molecular weight and molecular weight distribution have been carefully tailored to supply grades suitable for a variety of processing requirements and end-use applications. KYNAR® 740 is appropriate for use in most extrusion applications and can be injection molded. The powder form of this resin grade is available as KYNAR® 741 PVDF. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 6.0 to 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 44.8 to 55.2 | MPa | |
| Break, 23°C | 34.5 to 55.2 | MPa | |
| Tensile Elongation (Break, 23°C) | 20 to 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1380 to 2310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 58.6 to 75.8 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 68.9 to 103 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 165 to 172 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 1500 to 2300 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 4050 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Celstran® PBT-GF50-08 | Celanese Corporation | PBT | Celstran® |
| Fainplast PVC RH 704 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Latistat 62-08 | LATI S.p.A. | Nylon 6 | Latistat |
| ARLEN™ E440NK | Mitsui Chemicals, Inc. | Nylon 6T | ARLEN™ |