Isocor™ HW115SI
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Shakespeare Monofilaments and Specialty Polymers |
| Trademark: | Isocor™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BOUSpR_Isocor-HW115SI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Isocor™ HW115SI is a high viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption, greater dimensional stability, and improved abrasion resistance. This resin can be processed using conventional techniques. Typical applications for HW115SI include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.07 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | -- | 1.4 | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 60.0 | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | 300 | % | ASTM D638 |
| Flexural Modulus | 2000 | 1300 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles) | 6.00 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 48 | 200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 175 | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.1 | 60.0 | °C | ASTM D648 |
| Melting Temperature | 215 | -- | °C | DSC |
| Injection | Dry | Unit | |
|---|---|---|---|
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 79.4 | °C | |
| Rear Temperature | 221 - 243 | °C | |
| Middle Temperature | 227 - 260 | °C | |
| Front Temperature | 238 - 271 | °C | |
| Nozzle Temperature | 238 - 271 | °C | |
| Processing (Melt) Temp | 238 - 271 | °C | |
| Mold Temperature | 10.0 - 93.3 | °C | |
| Injection Pressure | 3.45 - 13.8 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 | MPa |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 79.4 | °C | |
| Cylinder Zone 1 Temp. | 254 | °C | |
| Cylinder Zone 2 Temp. | 266 | °C | |
| Cylinder Zone 3 Temp. | 271 | °C | |
| Cylinder Zone 4 Temp. | 271 | °C | |
| Die Temperature | 271 | °C |
| Extrusion instructions |
|---|
| Flange: 500°F (260°C)Air Dew Point (max): 0°F (-18°C)Neck: 500°F (260°C)Head: 480°F (250°C)Pump: 480°F (250°C)L/D Ratio: 24 to 30:1Compression Ratio: 3.5:1Polymer @ Die: 430°F (220°C)Screw Pressure: 2000 psi |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8347-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vi-Chem PVC 80 Durometer Black | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Nypol® PA B3 G30 PRTA011 NT303 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| LNP™ THERMOCOMP™ SF004S compound | SABIC Innovative Plastics | Nylon 12 | LNP™ THERMOCOMP™ |
| LEXAN™ OQ4320R resin | SABIC Innovative Plastics | PC | LEXAN™ |