Kinta FR6000 is a polyamide 6 (nylon 6) product,. It is available in the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 - 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 15 | % | ASTM D638 |
| Flexural Modulus 3 | 3100 | MPa | ASTM D790 |
| Flexural Strength 4 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 5.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 85.0 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| CLTE - Flow | 2.0E-5 - 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dissipation Factor 5(23°C, 1 MHz) | 0.030 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Injection Pressure | 100 - 160 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Colorite Rigid PVC 1127A-012 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Hyundai EP PA66 LD380 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| LNP™ LUBRICOMP™ RX03643H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Luen Kee A-Grade | Luen Kee Plastic Materials Factory Limited | PC | Luen Kee |
| Plenco 04504 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |