Stanyl® TE373
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BN9p8E_Stanyl-TE373.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TE373 is a Polyamide 46 (Nylon 46) material. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TE373 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.17 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.0 | -- | % | |
| Flow | 2.0 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2800 | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 10 | 15 | % | ISO 527-2 |
| Flexural Modulus | 2400 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 5.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | 120 | kJ/m² | |
| 23°C | 150 kJ/m² | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 5.0 | 9.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 HF | RTP Company | PEEK | RTP |
| RTP 107CC Z | RTP Company | PP Homopolymer | RTP |
| TPV Elastoprene® N40D-S | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Adell Polyolefin ZS-10 | Adell Plastics, Inc. | Polyolefin, Unspecified | Adell Polyolefin |
| Glasrod HIR | Glastic Corporation | Polyester, TS | Glasrod |