Vyncolit® TX10916
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BMinNY_VyncolitTX10916.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® TX10916 is a graphite filled phenolic molding compound with excellent dimensional stability and a low coefficient of friction. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.44 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.080 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.62 | % | ISO 178 |
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.47 | % | ISO 527-2 |
| Flexural Modulus | 15000 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Compressive Stress | 162 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 2.9 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 166 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 2.0E-5 | cm/cm/°C | TMA |
| Lateral | 2.8E-5 | cm/cm/°C | TMA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G15 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Chiao Fu PA66 MD312G33 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Hipolyene 1532 MS | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Plasmer 2065N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 9604-85 Green 3198 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |