LNP™ STAT-KON™ DEL329E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BM03wm_LNPSTATKONDEL329Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DEL329E is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Internally Lubricated. Also known as: LNP* STAT-KON* Compound DCL-4032 EM FR Product reorder name: DEL329E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7370 | MPa | ASTM D638 |
| -- | 7110 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 95.0 | MPa | ASTM D638 |
| Fracture | 93.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.3 | % | ASTM D638 |
| Fracture | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 6320 | MPa | ASTM D790 |
| -- 5 | 6540 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 140 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 143 | MPa | ASTM D790 |
| Fracture, 50.0mm span 7 | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 63 | J/m | ASTM D256 |
| 23°C 8 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 9 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 17.0 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 149 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 146 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 145 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 7.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 - 6.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAKEEP® 2000P | Evonik Industries AG | PEEK | VESTAKEEP® |
| Clariant Nylon 6/6 6608M33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ELASTOSIL® LR 3003/10 TR A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Hifax EYS 145P Black | LyondellBasell Industries | PP Copolymer | Hifax |
| MAJORIS FT103C | AD majoris | PP, Unspecified | MAJORIS |