LNP™ THERMOTUF™ MF004AI compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BLRveF_LNP-THERMOTUF-MF004AI-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF MF004AI is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound MF-1004 HI Product reorder name: MF004AI |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.1 to 1.3 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 to 1.3 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4830 | MPa | ASTM D638 |
| -- | 4940 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 40.0 | MPa | ASTM D638 |
| Break | 37.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 4.8 | % | ASTM D638 |
| Break | 4.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 41.4 | MPa | ASTM D790 |
| -- | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 2 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 151 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 144 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 109 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 104 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT5100-04 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Tectron H2245 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Ebalta LH 25 / LH 25 L | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| LNP™ THERMOCOMP™ RF007SXQ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 6238-75 Red 6302 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |