Asaflex™ 815
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Asaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BKdOM7_Asaflex-815.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sheet grade. Blended with SC*, for highly transparent sheets. It is supplied in pellet form. Blended with SC* for transparent blister packs and other sheets, with GPPS for frozen dessert cups and other containers, and with GPPS/Tufprene™ to obtain PS sheets for food containers and other applications. * Styrenic copolymer from PS Japan Corp. similar to Asaflex™ 815 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS (general-purpose polystyrene). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ISO 2039-2 | |
| Shore Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 200 | % | ISO 527-2/5 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Complete Break) | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Complete Break) | 100 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 82.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 90.0 | % | ISO 3537 |
| Haze (2000 µm) | 0.50 | % | ISO 3537 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Megalon® 122C | Mega Polymers | Nylon 66 | Megalon® |
| Witcom PPA 6LC-HS | Witcom Engineering Plastics B.V. | PPA | Witcom PPA |
| Multi-Flex® TPE D3604 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Durethan® BKV 15 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Plaslube® PA6/6,6 L N | Techmer Engineered Solutions | Nylon 66/6 | Plaslube® |