KOPELEN BM-311
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | KOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BKQL9p_KOPELEN-BM-311.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BM-311 is impact block copolymer which has ethylene-propylene rubber inside homo polypropylene. This grade can be processed by sheet extrusion. B-310 shows good impact resistance at low temperature and has also high strength. It has good vacuum molding property, suitable for the production of vacuum molding goods. BM-311 is applied to food packaging tray, various industrial sheets, conjugated duct. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1080 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C | 59 | J/m | ASTM D256 |
| 23°C | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ExTima™ GP MB PC 330 | Ovation Polymers Inc. | PC | ExTima™ |
| ESENTTIA 02H82-AC | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| KOPA® KN111 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ STAT-KON™ DEF13 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| MAJORIS DE101 - 8229 | AD majoris | PP, Unspecified | MAJORIS |