| ADMER® AT1404E is an maleic anhydride grafted, co-PP based tie resin, suitable for high performance coating and extrusion applications such a pipes and injection molding. It offers strong adhesion to PA, EVOH and Aluminum. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 18.0 | MPa | |
| Break | 28.0 | MPa | |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (Area) | 0.300 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Peak Melting Temperature | 146 | °C | ASTM D3418 |
| Oxidation Induction Time (210°C) | 5.0 | min | ISO 11357-6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 70836 B | RTP Company | PP, Unspecified | RTP |
| SABIC® PP 90910 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PP |
| VEGEMAT® E4589 | VEGEPLAST S.A.S. | Biodeg Polymers | VEGEMAT® |
| Evoprene™ GC 5689 | AlphaGary | SEBS | Evoprene™ GC |
| Petlon R-Prime F3-T40-00-BK | Petlon Polymers Ltd | PP, Unspecified | Petlon R-Prime |