UmaPET HSI/HSO
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | UmaPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BHgnGY_UmaPET-HSI-HSO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
KEY FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0120 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0150 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0200 mm | 2.0 | % | |
| Flow : 150°C, 30 min, 0.0250 mm | 2.0 | % | |
| Across Flow : 150°C, 30 min, 0.0120 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0150 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0200 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0250 mm | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.45 | ||
| vs. Itself - Dynamic 2 | 0.45 | ||
| vs. Itself - Dynamic 3 | 0.45 | ||
| vs. Itself - Dynamic 4 | 0.45 | ||
| vs. Itself - Static 5 | 0.55 | ||
| vs. Itself - Static 6 | 0.55 | ||
| vs. Itself - Static 7 | 0.55 | ||
| vs. Itself - Static 8 | 0.55 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 15 20 25 | µm | |
| Film Thickness - Recommended / Available | 12, 15, 20, 25 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Break, 12 µm | 177 | MPa | |
| MD : Break, 15 µm | 177 | MPa | |
| MD : Break, 20 µm | 172 | MPa | |
| MD : Break, 25 µm | 172 | MPa | |
| TD : Break, 12 µm | 186 | MPa | |
| TD : Break, 15 µm | 186 | MPa | |
| TD : Break, 20 µm | 181 | MPa | |
| TD : Break, 25 µm | 181 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 100 | % | |
| MD : Break, 15 µm | 100 | % | |
| MD : Break, 20 µm | 100 | % | |
| MD : Break, 25 µm | 100 | % | |
| TD : Break, 12 µm | 90 | % | |
| TD : Break, 15 µm | 90 | % | |
| TD : Break, 20 µm | 90 | % | |
| TD : Break, 25 µm | 90 | % | |
| Yield | Internal Method | ||
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 20.0 µm | 35.7 | m²/kg | |
| 25.0 µm | 28.6 | m²/kg |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Strength 9 | Internal Method | ||
| 140°C, 12.0 µm | 393.7 | g/2.5 cm | |
| 140°C, 15.0 µm | 492.1 | g/2.5 cm | |
| 140°C, 20.0 µm | 492.1 | g/2.5 cm | |
| 140°C, 25.0 µm | 590.6 | g/2.5 cm | |
| Wetting Tension - Plain side | ASTM D2578 | ||
| 10.0 µm | 44 | dyne/cm | |
| 12.0 µm | 44 | dyne/cm | |
| 15.0 µm | 44 | dyne/cm | |
| 23.0 µm | 44 | dyne/cm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 12.0 µm | 3.0 | % | |
| 15.0 µm | 3.0 | % | |
| 20.0 µm | 3.5 | % | |
| 25.0 µm | 40 | % |
| Note Message | |
|---|---|
| 1 . | 12 µm |
| 2 . | 20 µm |
| 3 . | 15 µm |
| 4 . | 25 µm |
| 5 . | 20 µm |
| 6 . | 12 µm |
| 7 . | 15 µm |
| 8 . | 25 µm |
| 9 . | Seal to seal surface, 2s, 3 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® F-3067 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| Surlyn Reflection Series® SURSG201UN-10T | LTL Color Compounders, Inc. | Nylon 6 Alloy | Surlyn Reflection Series® |
| Sylvin 9659-55 Yellow 4166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TF2CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| CP PRYME® ABS A100-20 | Chase Plastics Services Inc. | ABS | CP PRYME® ABS |