TECHNYL® eXten D 458P BLACK
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® eXten |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BHMoDO_TECHNYL-eXten-D-458P-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® eXten D 458P is a high viscosity unfilled plasticized PA6.10 for extrusion applications. The product is also UV stabilized. It is a partially bio-sourced material. It is available in natural and black colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 3.1 | -- | % | |
| Flow | 3.5 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.46 | -- | % | |
| Saturation, 23°C | 1.8 | -- | % | |
| Molding Shrinkage Isotropy | 1.16 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 800 | 550 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 35.0 | -- | MPa | |
| Break | 40.0 | 34.0 | MPa | |
| Tensile Strain (Break) | 150 | 240 | % | ISO 527-2/1A |
| Flexural Modulus | 690 | 530 | MPa | ISO 178 |
| Flexural Stress | 30.0 | 22.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 19 | kJ/m² | |
| 23°C | 87 | 120 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 51.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 215 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 205 to 225 | °C | |
| Cylinder Zone 3 Temp. | 215 to 235 | °C | |
| Cylinder Zone 5 Temp. | 220 to 240 | °C | |
| Die Temperature | 215 to 235 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F086-HHH-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| New-prene™ 6190B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| AKROMID® A3 GF 40 1 black (2386) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| LEXAN™ 943 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ THERMOCOMP™ RF005SXS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |