Lustran® ABS 552
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BGi5OZ_Lustran-ABS-552.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran ABS 552 resin is a medium-gloss, medium-impact extrusion grade of ABS (acrylonitrile butadiene styrene). It provides a good balance between rigidity and impact strength, and has a stiff melt flow suitable for extrusion and thermoforming. Lustran ABS 552 resin is easy to color with ABS color concentrates. This resin is designed for either profile extrusion or substrate coextrusion and can be used alone or blended with a higher-impact resin. As with any product, use of Lustran ABS 552 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Specific Volume | 0.950 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 6.0 | g/10 min | ASTM D1238 |
| 230°C/10.0 kg | 11 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 35.9 | MPa | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 59.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -34°C, 3.18 mm | 100 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 260 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -34°C, Peak Energy | 12.0 | J | ASTM D3763 |
| -34°C, Total Energy | 13.0 | J | ASTM D3763 |
| -18°C, Peak Energy | 17.0 | J | ASTM D3763 |
| -18°C, Total Energy | 21.0 | J | ASTM D3763 |
| 23°C, Total Energy | 32.0 | J | ASTM D3763 |
| 23°C, Peak Energy | 22.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 93.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 87.8 | °C | ASTM D648 |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 60.0 | °C | UL 746 |
| RTI (1.50 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, NC) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60, extruded sheet | 90 | ASTM D523 | |
| 60, thermoplastic | < 20 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 216 - 241 | °C | |
| Cylinder Zone 2 Temp. | 216 - 241 | °C | |
| Cylinder Zone 3 Temp. | 216 - 241 | °C | |
| Cylinder Zone 4 Temp. | 216 - 241 | °C | |
| Cylinder Zone 5 Temp. | 216 - 241 | °C | |
| Melt Temperature | 216 - 249 | °C | |
| Die Temperature | 210 - 241 | °C | |
| Take-Off Roll | 62.8 - 104 | °C |
| Extrusion instructions |
|---|
| Compression Ratio: 2.5:1 to 2.7:1Pump Ratio: 1.5 to 2.0L/D Ratio: 15:1 to 20:1Max Regrind Allowed: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 10 Z | RTP Company | Nylon 66 | RTP |
| SUSTAMID 6G HS | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Wellamid® MR410 22H-GY1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Okirol® E-6F | DIOKI d.d. | PS (EPS) | Okirol® |
| Integra™ PC-5017 U | PolySource, LLC | PC | Integra™ |