Epocast 8623-A/Hardener 9861
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BGZa66_Epocast-8623-A-Hardener-9861.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 8623-A resin/Hardener 9861 epoxy syntactic is a two-part, core-filling compound with a soft paste consistency for easy extrusion through a 1/8-in. (3mm) nozzle. Epocast® 8623-A resin/Hardener 9861 epoxy syntactic is self-extinguishing and cures at room temperature, if desired. Elevated temperature cure or post cure will improve elevated temperature properties. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.650 | g/cm³ | ASTM D792 |
| -- 2 | 0.700 | g/cm³ | ASTM D792 |
| -- 3 | 1.05 | g/cm³ | ASTM D792 |
| Solids Content 4 | 100 | % | ASTM D1644 |
| Viscosity | ASTM D2393 | ||
| -- 5 | Paste | ASTM D2393 | |
| -- 6 | Soft-paste | ASTM D2393 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| flammability- self extinguishing time | sec | BMS 5-28 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 100 gms (25°C) | 40.0 - 60.0 | min | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 1.0 | day | |
| Extrudability - 1/8 inch nozzle at 80 psi 7 | 30.0 | g/min | |
| Tensile Lap Shear - etched al/al (25°C) | 11.0 | MPa | ASTM D1002 |
| Weight Gain 8 | ASTM D570 | ||
| Distilled water | 1.5 | % | ASTM D570 |
| Mil-M-5606, hydraulic fluid | 0.40 | % | ASTM D570 |
| Mil-S-3136, Type III test fluid : 25°C | 0.30 | % | ASTM D570 |
| Skydrol 500-A | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 1720 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 34.5 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 20 | ||
| Thermoset Mix Viscosity 9(25°C) | 18000 | cP | ASTM D2393 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 24 hours at 77°F (25°c), or gel at 77°F (25°c), plus 1 hour at 180-200°F (83-93°c). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | System |
| 5 . | Resin |
| 6 . | System |
| 7 . | System |
| 8 . | on immersion - 24 hrs |
| 9 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPOA10400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| BMC 102 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| AMTOPP SP30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Arak LLDPE HD6070EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Chemical Resources PA66101 | Chemical Resources, Inc. | Nylon 66 | Chemical Resources |