CALIBRE™ 893-10
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BGYqZN_CALIBRE-893-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 891-10 Series provides superior ignition resistance in opaque applications. The CALIBRE 891-10 series products are available in 2 additive packages: CALIBRE 891: Mold release, CALIBRE 893: Mold release and UV stabilizer. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 16.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570, ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 59 | ||
| R-Scale | 123 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2380 | MPa | ASTM D638 |
| -- | 2380 | MPa | ISO 527-2/50 |
| -- | 2300 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield 5 | 61.4 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Yield | 60.0 | MPa | ISO 527-2 6 |
| Break 7 | 58.6 | MPa | ASTM D638 |
| Break | 59.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2 8 |
| Break 9 | 120 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 10 |
| Flexural Modulus | |||
| -- 11 | 2330 | MPa | ASTM D790 |
| -- | 2330 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 12 | 97.9 | MPa | ASTM D790 |
| -- | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 13 | ||
| -30°C | 15.0 | kJ/m² | |
| 23°C | 30.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 14 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D256 |
| 23°C | 68 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact 15(23°C, Total Energy) | 62.1 | J | ASTM D3763 |
| Tensile Impact Strength | 630 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648 |
| 1.8 MPa | 127 | °C | ISO 75-2 16 |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525 17 |
| 50°C/h, B (50N) | 151 | °C | ISO 306 18 |
| CLTE - Flow | |||
| -- | 6.5E-5 | cm/cm/°C | ASTM D696 |
| -- | 7.0E-5 | cm/cm/°C | ISO 11359-2 19 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 20 | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.20 mm | V-0 5VA | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | V-0 | ISO 1210 21 | |
| Burning Behav. at thickness h (3.20 mm, UL) | V-0 | ISO 1210 22 | |
| Burning Behav. 5V at thickness h (3.20 mm, UL) | 5VA | ISO 10351 23 | |
| Oxygen Index 24 | 36 | % | ASTM D2863, ISO 4589-2 3 25 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 51 mm/min |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 51 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 51 mm/min |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 51 mm/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Method I (3 point load), 2.0 mm/min |
| 12 . | Method I (3 point load), 2.0 mm/min |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | 3.39 m/sec |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Loading 2 (50 N) |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 24 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 25 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® OF 803M | ELASTO | TPE | Mediprene® |
| Niuk 60GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | PBT | Niuk |
| Chemical Resources SAN900 | Chemical Resources, Inc. | SAN | Chemical Resources |
| Kumho SBR 1763 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| KEBAFORM® C 901 CB | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |