Kumho EP HGX4500
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Korea Kumho Petrochemical Co., Ltd. |
| Trademark: | Kumho EP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BGRQae_Kumho-EP-HGX4500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Features: Ultra high heat resistance Applications: Automobile parts, Mirror housing, Radiator grills, Rear lamp housings |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/21.6 kg | 4.5 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.80 | % | ASTM D955 |
| -- | 0.50 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 42.2 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 15 | % | ASTM D638 |
| Break | 17 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2160 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 64.0 | MPa | ISO 178 |
| Yield | 60.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 160 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 140 | J/m | ASTM D256 |
| 23°C | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118 Series | SABIC Americas, Inc. | LLDPE | SABIC® LLDPE |
| megol® SV/PS 50 | API SpA | SEBS | megol® |
| TRANSMARE® 10HGF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Ultramid® TG7S | BASF Corporation | Nylon 6 | Ultramid® |
| OTECH TPE OW138 - Cable Jacket | OTECH Corporation | TPE | OTECH TPE |