CYCOLAC™ HMG47MD resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BG6kNu_CYCOLACHMG47MDresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
General purpose, injection molding ABS for medical applications. Biocompatible (ISO10993). FDA compliant. Gamma & EtO sterilizable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 5.6 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2280 | MPa | ASTM D638 |
| -- | 2530 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 44.1 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 33.8 | MPa | ASTM D638 |
| Fracture | 35.3 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/5 |
| Fracture 5 | 24 | % | ASTM D638 |
| Fracture | 25 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2340 | MPa | ASTM D790 |
| -- 7 | 2410 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 76.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 320 | J/m | ASTM D256 |
| -30°C 9 | 8.5 | kJ/m² | ISO 180/1A |
| 23°C 10 | 23 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 31.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 12 |
| -- | 100 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 188 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Nozzle Temperature | 218 - 260 | °C | |
| Processing (Melt) Temp | 218 - 260 | °C | |
| Mold Temperature | 48.9 - 71.1 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7A21-3000 | Spartech Polycom | PC+PBT | Spartech |
| NuSil CV-1146-2 | NuSil Technology | Silicone | NuSil |
| Allen 6000 | SEKISUI Polymer Innovations, LLC | ABS+Acrylic | Allen |
| Kingfa FRHIPS-980 | Kingfa | PS (HIPS) | Kingfa |
| LNP™ FARADEX™ AS002 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |