NOVAPOL® LF-Y320 Series
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BG5CMh_NOVAPOL-LF-Y320-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LF-Y320-A (Barefoot resin): Industrial packaging, liners, shrink film, blends with LLDPE LF-Y320-C (Antiblock only): Industrial packaging, liners, shrink film, blends with LLDPE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Thickness - Recommended / Available | > 38µm | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 190 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 230 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 16.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 21.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 110 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 450 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 320 | g | ASTM D1922 |
| TD : 38 µm, blown film | 120 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 20 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 30 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (38.0 µm) | 90.0 | J/cm | Internal method |
| Extrusion instructions |
|---|
| Optimum Blow-up Ratio: 2:1 to 3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM A3 MF PRTA010 PR304 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Homopolymer | Tenopom® POM |
| TABOREN PC 79 C 40 | SILON s.ro | PP Copolymer | TABOREN |
| THERMOLAST® K TF3CGN (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Yuyao PBT 3055G30 | Yuyao Tenglong Plastics Co., Ltd. | PBT | Yuyao PBT |
| NOVALAC RX®873 | Vyncolit N.V. | Phenolic | NOVALAC |