Bayblend® T65 AT
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BG2uuP_Bayblend-T65-AT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 temperature = 121 °C; improved antistatic behavior; good flow. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 260°C, 3.00 mm | 0.65 to 0.85 | % | |
| Flow : 260°C, 3.00 mm | 0.65 to 0.85 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 52.0 | MPa | |
| Break, 23°C | 52.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.8 | % | |
| Break, 23°C | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 124 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 119 | °C | ISO 306/B50 |
| -- | 121 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.850 mm, Bayer Test) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 210 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silplus® 60 CW | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| MOSTEN MT 935 | UNIPETROL RPA | PP Random Copolymer | MOSTEN |
| NYCOA Polyamide 2061 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| Lifoflex® UV FLAM 40600 | Müller Kunststoffe GmbH | TPE | Lifoflex® |
| Hifax TRC 277P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |