Ebalta SG 700 A / PUR 5
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BG027T_Ebalta-SG-700-A-PUR-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta SG 700 is a two-component-Polyurethane casting resin, which cures very fast at room temperature. The very good workability and the excellent mechanical properties makes SG 700 a material with versatile application possibilities. ebalta SG 700 A is even more abrasion-resistant, but not so well workable by machine. Displacements, even made of wood, can be filled in. Material should be carefully stirred up/ shaked before use. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 to 86 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 4020 to 4920 | MPa | ISO 178 |
| Flexural Stress | 38.0 to 48.0 | MPa | ISO 178 |
| Compressive Stress | 48.0 to 58.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 3.7 to 5.7 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 47 to 51 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 15 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.70 to 1.80 | g/cm³ | |
| Viscosity (25°C) | 1.5 to 2.2 | Pa·s | |
| Curing Time (20°C) | 1.0 to 2.0 | hr | |
| Pot Life 1(20°C) | 5.0 to 7.0 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ K130HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| Ad-Tech Epoxy CER-112-1 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Formolene® 6507N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Hostaform® MT8F01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ VERTON™ MV008SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |