MAJORIS FG100X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BF8tRC_MAJORIS-FG100X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS FG100X is a high performance reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. MAJORIS FG100X has been developed especially for demanding applications in various engineering sectors. MAJORIS FG100X has very high rigidity and impact strength, good dimensional stability and creep resistance also at high temperature. APPLICATIONS Product requiring, such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.997 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3390 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3220 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 168 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 154 | °C | ISO 75-2/A |
| Ball Pressure Test (140°C) | Pass | NF C 61-303 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silplus® 80 HS | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Nanjing Hongrui PA66 A1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| AKROMID® B3 GF 40 S1 black (3384) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Geon™ BIO RC6500 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| OXNILON 66 20PTFE | Oxford Polymers | Nylon 66 | OXNILON 66 |