Moplen EP548S
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BEwY2m_Moplen-EP548S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP548S is a nucleated heterophasic copolymer with antistatic agent used for injection moulding applications. It exhibits an outstanding balance of mechanical properties combined with a medium high fluidity. Moplen EP548S is extensively used in housewares and in thin-walled containers for food packaging (e.g. margerine tubs, yoghurt pots, etc.). Moplen EP548S is suitable for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 44 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 59.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 68.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1550 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 30 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.0 | kJ/m² | |
| 0°C | 3.5 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 85 | kJ/m² | |
| 0°C | 100 | kJ/m² | |
| 23°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -53.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A50 |
| -- | 80.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 12CGF30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Vydyne® R543 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Next Nylon 66 Prime Series PMG38-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| BAAF UHMW-PE M-2 | BAAF | HDPE, UHMW | BAAF UHMW-PE |
| Badaflex® TPE-S 60A 5123 FR S1 | Bada AG | TPE | Badaflex® |