RTP 101 HB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BEgU7W_RTP-101-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - UL94 HB |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2960 | MPa | ASTM D638 |
| Tensile Strength | 38.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 7.5 to 8.5 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 55.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 132 | °C | |
| 1.8 MPa, Unannealed | 129 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 57 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Spartech Polycom E65080 | Spartech Polycom | PVC, Unspecified | Spartech |
| Estane® 58325 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| HiFill® POM HO GF15 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |
| OTECH PVC OE6537 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |