LNP™ THERMOCOMP™ KFB11 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BEgNKe_LNPTHERMOCOMPKFB11compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KFB11 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled. Also known as: LNP* THERMOCOMP* Compound KFX-1002 MG Product reorder name: KFB11 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.0 - 3.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 3.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.7 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 4100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 64.8 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2 |
| Fracture | 62.1 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 5.7 | % | ASTM D638 |
| Fracture | 7.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D4812 |
| 23°C 3 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.60 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 163 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 161 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 153 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 150 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer E70K | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| Caltex PP MT61HS | GS Caltex | PP, Unspecified | Caltex PP |
| Asaflex™ 845 | AKelastomers | SBS | Asaflex™ |
| EvoSource™ ABS 4535 70/05 | MBA Polymers | ABS | EvoSource™ |
| EMERGE™ PC 8701 | Trinseo | PC | EMERGE™ |