LNP™ THERMOTUF™ PF008IR compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BDpYeL_LNP-THERMOTUF-PF008IR-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF PF008IR is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: High Impact, Mold Release. Also known as: LNP* THERMOTUF* Compound PF-1008 HI MR Product reorder name: PF008IR |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 143 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 9860 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 206 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOLIT® M 5761 | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| VALOX™ V2000DM resin | SABIC Innovative Plastics | PBT | VALOX™ |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8854 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Hyundai EP PA6 LS280 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Sylvin 9915-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |