LUBEMIX 85 BLACK
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BDR7W9_LUBEMIX-85-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on blend PC/ABS second choice. Black coloured. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 to 1.17 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 to 20 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 to 2500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 50.0 to 55.0 | MPa | |
| Break | 45.0 to 50.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 6.0 to 8.0 | % | |
| Break | 45 to 50 | % | |
| Flexural Modulus 1 | 1800 to 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 55.0 to 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 to 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 450 to 500 | J/m | ASTM D256A |
| 23°C 3 | No Break | ASTM D256 | |
| 23°C | 40 to 45 | kJ/m² | ISO 180/A |
| 23°C 4 | 45 to 50 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 115 to 125 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 120 to 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 100 to 110 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 125 to 135 | °C | ISO 306/A120 |
| -- | 120 to 130 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME PP SP5665 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| Elastron® G G601.A45.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Eltex® A5006PFN1281 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| LNP™ THERMOCOMP™ WF006H compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| Tunhe PBT TH6075 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |