BJB Polyurethane WC-540 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BD60ef_BJB-Polyurethane-WC-540-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WC-540 A/B is a two-part, water clear, colorless aliphatic based polyurethane elastomer. It is recommended for use whenever a flexible, permanently transparent elastomer is required. It is UV light and oxidation resistant and can be easily tinted or pigmented to clean bright colors. WC-540 A/B does not contain MOCA, TDI or MDA. In addition to being an excellent castable product, it also functions well as a solvent-free adhesive for bonding various substrates. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.02 | g/cm³ | |
| -- | 1.06 | g/cm³ | |
| -- 2 | 1.08 | g/cm³ | |
| Specific Volume | 0.950 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 30.0 | min | |
| Work Time 3(25°C) | 20.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 35 to 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 2.69 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 300 | % | ASTM D412 |
| Tear Strength 4 | 7.53 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 4.13 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.095 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 50, Mix Ratio by Volume: 48 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 5 | 910 | cP | |
| 25°C 6 | 375 | cP | |
| 25°C 7 | 2120 | cP | |
| Demold Time (25°C) | 480 to 720 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Die C |
| 5 . | Mixed |
| 6 . | Part B |
| 7 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF33-66/6 XE-N | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| Ultralloy™ 108 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| ESTAPROP 1000 V2 K | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Geon™ Vinyl Rigid Molding M5730 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| NYLOY® MG-0025N-V0 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |