Latamid 66 H-V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BB5fxf_Latamid-66-H-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Heat stabilised. UL94 V-0 classified, halogens and red phosphorus free. Product UL certified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 1.1 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 4200 | MPa | |
| 60°C | 2000 | MPa | |
| 90°C | 1200 | MPa | |
| 120°C | 900 | MPa | |
| 150°C | 700 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 75.0 | MPa | |
| Break, 23°C | 70.0 | MPa | |
| Break, 60°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 8.0 | % | |
| Break, 60°C | 45 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 100 | °C | |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A MV 14 FR 1 | A. Schulman Europe | PBT | SCHULADUR® |
| SumiDurez PM 9750 | SumiDurez Singapore Pte Ltd | Phenolic | SumiDurez |
| VESTOSINT® 2070 natural color | Evonik Industries AG | Nylon 12 | VESTOSINT® |
| LEXAN™ XLS1210 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LubriOne™ LubriOne NY-30GF/15T/02S natur | PolyOne Corporation | Nylon 6 | LubriOne™ |