BCC Resins BC 6004

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	BCC Products Inc.
Trademark:	BCC Resins
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BAP5im_BCC-Resins-BC-6004.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
BC 6004 is a white thixotropic epoxy surface coat that had the ability to cure and bond to freshly poured wet plaster. This formulated resin compound can be applied with a brush or troweled to a thickness of 1/8" or less on vertical surfaces or over sharp radii without sag or fear of run-off. BC 6004 features moderate heat resistance and tracing hardness. Procedure for Plastic Faced Plaster Applications: BC 6004 should be applied over a properly mold-released surface so that positive removal of the surface coated plaster casting is assured. For best results, two coats approximately 1/16" thick should be used. The first coat should be brushed over the entire surface and then allowed to cure to a gelled or very tacky state. The second coat should be applied over the first. If hemp, glass or other fibrous plaster reinforcements are to be used, they should be placed in the freshly applied second coat immediately. Plaster can then be poured against the wet, second coat of BC 6004. To achieve good adhesion of the epoxy to the plaster, it is recommended that the plaster be poured immediately. The application of two coats of BC 6004 will eliminate surface porosity that sometimes occurs when fast setting, "hot" plaster compounds are cast over a single coat of epoxy.

Message

BC 6004 is a white thixotropic epoxy surface coat that had the ability to cure and bond to freshly poured wet plaster. This formulated resin compound can be applied with a brush or troweled to a thickness of 1/8" or less on vertical surfaces or over sharp radii without sag or fear of run-off. BC 6004 features moderate heat resistance and tracing hardness.

Procedure for Plastic Faced Plaster Applications:
BC 6004 should be applied over a properly mold-released surface so that positive removal of the surface coated plaster casting is assured. For best results, two coats approximately 1/16" thick should be used. The first coat should be brushed over the entire surface and then allowed to cure to a gelled or very tacky state. The second coat should be applied over the first. If hemp, glass or other fibrous plaster reinforcements are to be used, they should be placed in the freshly applied second coat immediately. Plaster can then be poured against the wet, second coat of BC 6004. To achieve good adhesion of the epoxy to the plaster, it is recommended that the plaster be poured immediately. The application of two coats of BC 6004 will eliminate surface porosity that sometimes occurs when fast setting, "hot" plaster compounds are cast over a single coat of epoxy.

General Information
Features	Medium Hardness Medium Heat Resistance Thixotropic
Uses	Coating Applications
Appearance	White
Forms	Paste
Processing Method	Coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.58	g/cm³	ASTM D792, ASTM D1505

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	89		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Ultimate)	46.9	MPa	ASTM D638
Flexural Modulus	6760	MPa	ASTM D790
Flexural Strength (Break)	59.3	MPa	ASTM D790
Compressive Strength	95.1	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	78.9	°C	ASTM D648

Thermoset	Nominal Value	Unit
Thermoset Components
Hardener	Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0
Resin	Mix Ratio by Weight: 12, Mix Ratio by Volume: 7.0
Pot Life (24°C)	15 to 20	min
Demold Time (24°C)	480 to 720	min

Resin Grade	Manufacturer	Category	Trademark
RTP 4086	RTP Company	PPA	RTP
NORYL™ PN275 resin	SABIC Innovative Plastics	PPE+PS	NORYL™
Borlink™ LE0592	Borealis AG	PE, Unspecified	Borlink™
GAPEX® RPP10EV02NA	Ferro Corporation	PP, Unspecified	GAPEX®
EnCom POM 0614 TF	EnCom, Inc.	Acetal (POM) Homopolymer	EnCom