Toyolac® 100G-30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BAHpd9_Toyolac100G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac®100G-30 is an acrylonitrile butadiene styrene (ABS) material, and the filler is 30% glass fiber reinforced material. This product is available in Europe or Asia Pacific,. Toyolac®The main features of 100G-30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 1 | 127 | MPa | ASTM D638 |
| Fracture | 107 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 2 | 3.0 | % | ASTM D638 |
| Fracture | > 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 3 | 8100 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 160 | MPa | ASTM D790 |
| -- 5 | 174 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 12.7 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 108 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 103 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 HI4 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| TPV Elastoprene® N40D-i | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| UNIVAL™ DMDB-6200 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| INSTRUC PSGF15 | Infinity LTL Engineered Compounds | PS (GPPS) | INSTRUC |
| Hostacom XBR 169 G G31463 | LyondellBasell Industries | PP Copolymer | Hostacom |