HIVAL® 500354
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Nexeo Solutions, LLC. |
| Trademark: | HIVAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B9hxS9_HIVAL-500354.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIVAL®500354 is a high density polyethylene material,. This product is available in North America and is processed by blow molding or extrusion. HIVAL®The main features of the 500354 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.38 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 25.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact | 64.1 | J/cm | ASTM D1822 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Barrel Temperature | 166 - 182 | °C | |
| Blow Molding Head Temperature | 191 | °C | |
| Blow Molding Mold Temperature | 16 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.9 | °C | ASTM D648 |
| Brittleness Temperature 1 | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 193 - 227 | °C | |
| Cylinder Zone 3 Temp. | 199 - 232 | °C | |
| Cylinder Zone 5 Temp. | 204 - 243 | °C | |
| Die Temperature | 210 - 232 | °C |
| Extrusion instructions |
|---|
| Extrusion: Screw L/D: 20:01 Compression Ratio: 2:1-3:1 Blow Moldig: Blow Air: 90 psi Pre Blow: 10 psi |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC104 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| Buna® EP G 6850 | LANXESS Corporation | EPDM | Buna® EP |
| Electrafil® PA6 CF30 TL10 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Infino FD-1112 | SAMSUNG SDI CO., LTD. | PC | Infino |
| Latilub 66-20T | LATI S.p.A. | Nylon 66 | Latilub |