Generic LCP - Glass Fiber
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B9ddet_Generic-LCP---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic LCP - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.46 - 1.76 | g/cm³ | ASTM D792 |
| 23°C | 1.61 - 1.81 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.013 - 0.31 | % | ASTM D955 |
| Transverse flow : 23°C | 0.35 - 1.3 | % | ASTM D955 |
| 23°C | 0.040 - 0.62 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.010 - 0.10 | % | ASTM D570 |
| 23°C, 24 hr | 0.010 - 0.040 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 105 | ASTM D785 | |
| 23°C | 54 - 86 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 11000 - 19000 | MPa | ASTM D638 |
| 23°C | 11800 - 15100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 126 - 157 | MPa | ASTM D638 |
| Fracture, 23°C | 130 - 200 | MPa | ISO 527-2 |
| 23°C | 103 - 167 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 2.5 | % | ASTM D638 |
| Fracture, 23°C | 0.80 - 5.1 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 3.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 9720 - 16900 | MPa | ASTM D790 |
| 23°C | 10300 - 20200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 114 - 188 | MPa | ASTM D790 |
| 23°C | 170 - 255 | MPa | ISO 178 |
| Yield, 23°C | 120 - 235 | MPa | ASTM D790 |
| Compressive Modulus (23°C) | 10000 - 14500 | MPa | ISO 604 |
| Compressive Stress (23°C) | 74.7 - 140 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 - 42 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 15 - 48 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 55 - 210 | J/m | ASTM D256 |
| 23°C | 12 - 45 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 61 - 560 | J/m | ASTM D256 |
| 23°C | 14 - 62 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 250 - 252 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 209 - 318 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 230 - 340 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 157 - 267 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 146 - 202 | °C | ISO 306 |
| Melting Temperature | 280 - 336 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 7.8E-6 - 1.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.0E-6 - 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.7E-5 - 6.4E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 1.7E-5 - 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 2.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+13 - 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+5 - 3.3E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 13 - 50 | kV/mm | ASTM D149 |
| 23°C | 20 - 46 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.10 - 4.70 | ASTM D150 | |
| 23°C | 3.80 - 4.31 | IEC 60250 | |
| 23°C | 3.62 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.024 - 0.033 | ASTM D150 | |
| 23°C | 9.3E-3 - 0.030 | IEC 60250 | |
| Arc Resistance | 123 - 186 | sec | ASTM D495 |
| Comparative Tracking Index | 125 - 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 45 - 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 150 | °C | |
| Drying Time | 3.0 - 8.2 | hr | |
| Suggested Max Regrind | 30 | % | |
| Hopper Temperature | 25.0 - 120 | °C | |
| Rear Temperature | 270 - 341 | °C | |
| Middle Temperature | 280 - 360 | °C | |
| Front Temperature | 285 - 377 | °C | |
| Nozzle Temperature | 290 - 375 | °C | |
| Processing (Melt) Temp | 285 - 383 | °C | |
| Mold Temperature | 40.0 - 115 | °C | |
| Injection Pressure | 95.2 - 120 | MPa | |
| Holding Pressure | 29.5 - 100 | MPa | |
| Back Pressure | 0.900 - 2.95 | MPa | |
| Screw Speed | 75 - 80 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic LCP - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 N | Nilit Plastics | Nylon 66 | POLYNIL® |
| Chemlon® 60AIM | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Electrafil® PA6/6 03002 CF | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| HiFill® PA6 GF30 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina BLUE COLOR CONCENTRATE 06/30-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |