LNP™ STAT-KON™ DX05042 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B8PYwD_LNP-STAT-KON-DX05042-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DX05042 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding. Also known as: LNP* STAT-KON* Compound DCFL-4024 EM Product reorder name: DX05042 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 157 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11300 | MPa | ISO 178 |
| Flexural Stress | 223 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 145 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 6457 | Covestro - Polycarbonates | PC | Makrolon® |
| Vexel B12GF30 | Custom Resins Group | PBT | Vexel |
| Geon™ Vinyl Flexible G92B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Geon™ Vinyl Flexible 90043 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Pier One POM AH500P BK | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |