Prime Tuff-X 200

Category:	Unspecified , Unspecified
Manufacturer:	Primex Plastics Corporation
Trademark:	Prime Tuff-X
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	B7NPq1_Prime-Tuff-X-200.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Prime Tuff-X 200 is an engineered alloy that fills the gap between engineered plastics and high performance Polyolefins. Prime Tuff-X 200 has a very low C.L.T.E., excellent impact, UV protection and is highly chemical resistant. Applications: Ideal for ; automotive, power tools, irrigation, electronics, lawn and garden and RV applications. Processing: Prime Tuff-X 200 is a Semi-crystalline material that behaves differently in the thermoforming process when compared to an amorphous material. Ideal forming conditions; Mold temp. 170-190°F, Sheet temp. 320-360°F, part removal temp.145-170°F. Aluminum temperature controlled grit blasted tools are preferred. Ceramic tools can also work well if it is glass bead blasted. Quartz or ceramic heaters are preferred when working with Tuff-X. Calrod heaters can sometimes be used but gas fired is not recommended. Finishing: Tuff-X 200 can be fabricated by using many techniques such as; drilling, routing, punching, sawing, laser or die cut. Mechanical screws and other type of fasteners may be used to join Tuff-X 200 parts together. It may also be bonded with certain types of adhesives. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Our Tuff-X 200 material will accept any color imaginable, furthermore, this product can be painted with a two part paint system. Tuff-X 200 is offered in gauges from .090 to .400 in. and in widths up to 120". Tuff-X 200 is offered in several different patterns that include; FL/HC, H/C, Diamond Plate, Smooth and Levant II.

Message

Prime Tuff-X 200 is an engineered alloy that fills the gap between engineered plastics and high performance Polyolefins. Prime Tuff-X 200 has a very low C.L.T.E., excellent impact, UV protection and is highly chemical resistant.

Applications:
Ideal for ; automotive, power tools, irrigation, electronics, lawn and garden and RV applications.

Processing:
Prime Tuff-X 200 is a Semi-crystalline material that behaves differently in the thermoforming process when compared to an amorphous material. Ideal forming conditions; Mold temp. 170-190°F, Sheet temp. 320-360°F, part removal temp.145-170°F. Aluminum temperature controlled grit blasted tools are preferred. Ceramic tools can also work well if it is glass bead blasted. Quartz or ceramic heaters are preferred when working with Tuff-X. Calrod heaters can sometimes be used but gas fired is not recommended.

Finishing:
Tuff-X 200 can be fabricated by using many techniques such as; drilling, routing, punching, sawing, laser or die cut. Mechanical screws and other type of fasteners may be used to join Tuff-X 200 parts together. It may also be bonded with certain types of adhesives.

Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process.

Colors, Textures and Capabilities:
Our Tuff-X 200 material will accept any color imaginable, furthermore, this product can be painted with a two part paint system. Tuff-X 200 is offered in gauges from .090 to .400 in. and in widths up to 120". Tuff-X 200 is offered in several different patterns that include; FL/HC, H/C, Diamond Plate, Smooth and Levant II.

General Information
Features	Good Chemical Resistance Good Colorability Good UV Resistance High Heat Resistance High Impact Resistance High Tensile Strength Low Temperature Impact Resistance Semi Crystalline
Uses	Automotive Applications Electrical/Electronic Applications Lawn and Garden Equipment Power/Other Tools Sporting Goods
Appearance	Colors Available
Forms	Sheet
Processing Method	Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.12	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	0.60	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	24.5	MPa	ASTM D638
Flexural Modulus	2120	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-30°C	64	J/m
23°C	830	J/m
Instrumented Dart Impact (-30°C)	5.76	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	101	°C
1.8 MPa, Unannealed	58.9	°C
CLTE - Flow	4.9E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating (> 1.50 mm)	HB		UL 94

Additional Information	Nominal Value	Unit
De-mold Temperature	63 to 77	°C
Mold Temperature (other)	77 to 88	°C
Sheet Temperature	160 to 182	°C

Resin Grade	Manufacturer	Category	Trademark
TEKAMID™ H12LW	Mando Advanced Materials Co., Ltd.	ABS+Nylon	TEKAMID™
TRIBOCOMP® PA66 GF30 TS13	EPIC Polymers	Nylon 66	TRIBOCOMP®
Lifoflex® GA 1040	Müller Kunststoffe GmbH	SEBS	Lifoflex®
LUVOCOM® 1301-8456	Lehmann & Voss & Co.	PPS	LUVOCOM®
SABIC® PC PC1003R resin	SABIC Innovative Plastics Asia Pacific	PC	SABIC® PC