Grivory® XE 5106 (GVL-4H V0) is a Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X) material filled with 40% long glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grivory® XE 5106 (GVL-4H V0) are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.30 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 265 | 250 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14500 | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | 2.4 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 25 | 25 | kJ/m² | |
| 23°C | 25 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 70 | kJ/m² | |
| 23°C | 70 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 210 | -- | °C | ISO 75-2/C |
| Maximum Use Temperature | Internal Method | |||
| Long Term | 100 to 120 | -- | °C | |
| Short Term | 220 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA66+PA6I/X, MFHR, 14-140N, GF40 FR(40) | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (1.60 mm) | V-0 5VA | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADEKA YT-101 | Adeka Corporation | PUR-Ester | ADEKA |
| Evoprene™ COGEE 683 | AlphaGary | SEBS | Evoprene™ COGEE |
| Exxtral™ Performance Polyolefin CNU012 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| KumhoSunny PBT/ABS HBG5720 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| Sylvin 2990-82 Clear 8463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |