Tufpet PBT G2815
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B6oi0L_Tufpet-PBT-G2815.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT G2815 is a Polybutylene Terephthalate (PBT) material filled with 15% glass fiber. It is available in North America for injection molding. Important attributes of Tufpet PBT G2815 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 98.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.4 | % | ASTM D638 |
| Flexural Modulus | 6370 | MPa | ASTM D790 |
| Flexural Strength | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 | J/m | ASTM D256 |
| Unnotched Izod Impact | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 215 | °C | |
| 1.8 MPa, Unannealed | 200 | °C | |
| Specific Heat | 1550 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM C177 |
| RTI Elec | UL 746 | ||
| 0.790 mm | 130 | °C | |
| 1.57 mm | 130 | °C | |
| 3.18 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.790 mm | 120 | °C | |
| 1.57 mm | 120 | °C | |
| 3.18 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.790 mm | 120 | °C | |
| 1.57 mm | 120 | °C | |
| 3.18 mm | 120 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Arc Resistance | 23.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.790 mm | V-0 | ||
| 1.57 mm | V-0 | ||
| 3.18 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6433 9710 | Supreme Petrochem Ltd. | PS (MIPS) | SUPREME Specialty PS |
| Chemical Resources SAN300 | Chemical Resources, Inc. | SAN | Chemical Resources |
| Elastron® G G500.A45.N.PS | Elastron USA, Inc. | SEBS | Elastron® G |
| Infino NE-1050 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| Sylvin 8260-75 Blue 8341 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |