DOW™ HDPE XDMA-1206 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | 陶氏高密度聚乙烯 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B6d0Ol_DOWHDPEXDMA1206NT7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
XDMDA-1206 NT 7 Experimental High Density Polyethylene (HDPE) Resin from Dow is intended for use in injection molding applications such as caps and closures and other injection molding applications. This resin has been designed to meet demanding performance requirements such as environmental stress crack resistance, stiffness, impact strength, while maintaining good processing characteristics.
Complies with:
Consult the regulations for complete details. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.8 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 12.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.9 | MPa | ASTM D638 |
| Fracture | 22.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 1100 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1070 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 84.1 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 72.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 131 | °C | Internal method |
| Additional Information |
|---|
| Plaque molded and tested in accordance with ASTM D4976. |
| Note Message | |
|---|---|
| 1 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM ABS 7520 | Ponachem Compound GmbH | ABS | PONACOM ABS |
| Reny® 1507 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Amilan® CM3001-N | Toray Resin Company | Nylon 66 | Amilan® |
| AT 505 | Celanese EVA Performance Polymers | LDPE | AT |
| Lucky Enpla LKI | Lucky Enpla Co LTD | ABS | Lucky Enpla |