Order Products : sales@su-jiao.com
Clariant Nylon 6 PA213G13
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B5ix13_Clariant-Nylon-6-PA213G13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant Nylon 6 PA213G13 is a polyamide 6 (nylon 6) material, which contains a 13% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The typical application field of Clariant Nylon 6 PA213G13 is: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4800 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35mm | 210 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 195 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Rear Temperature | 249 - 266 | °C | |
| Middle Temperature | 249 - 266 | °C | |
| Front Temperature | 254 - 271 | °C | |
| Nozzle Temperature | 254 - 274 | °C | |
| Processing (Melt) Temp | 254 - 271 | °C | |
| Mold Temperature | 79.4 - 121 | °C | |
| Injection Pressure | 8.27 - 13.8 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Injection instructions |
|---|
| This material should be dried in a dessicant dryer.Injection Pressure, Initial: 1200 to 2000 psiInjection Pressure, Secondary: 60% of Initial |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PP 2126 | MBA Polymers | PP Impact Copolymer | MBA PP |
| RheTech Polypropylene CC20P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Ferro PP TPP30AF11HB NATURAL | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hostaform® C 2521 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Karina BLACK PVC COMPOUND 750-48/1-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |