HAIPLEN H90 X2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B5VBhs_HAIPLEN-H90-X2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer flame retardant UL 94 V2 high flow. UL94 V2 - all colors - 1,5 mm (yellow card) Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D), low blooming(LB) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.3 | % | |
| Across Flow | 1.3 | % | |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -23°C | 25 | J/m | ISO 180, ASTM D256 |
| 0°C | 35 | J/m | ISO 180, ASTM D256 |
| 23°C | 45 | J/m | ASTM D256, ISO 1798 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 120 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 3 1 |
| -- | 94.0 | °C | ASTM D1525, ISO 306/B 4 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Needle Flame Test | VDE 0471/2 | ||
| 1.60 mm | Pass | ||
| 3.20 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2207 HF UP | RTP Company | PEEK | RTP |
| Telcar® TL-2625A | Teknor Apex Company | TPE | Telcar® |
| Ultrason® E 2010 C6 | BASF Corporation | PESU | Ultrason® E |
| Geon™ Vinyl Rigid Extrusion L6607 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hanwha Total PP TB72P | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |