Reny® NXG5050NF
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B4r264_Reny-NXG5050NF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® NXG5050NF is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® NXG5050NF: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 3.7 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 2.10 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 198 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Flexural Modulus | 18200 | MPa | ISO 178 |
| Flexural Stress | 348 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 67 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 219 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.0E-5 | cm/cm/°C | |
| Transverse | 4.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (2.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5420 A1 | Spartech Polycom | PP, Unspecified | Spartech |
| Gebalon PC ULtimate G10 FR(y) | geba Kunststoffcompounds GmbH | PC | Gebalon |
| Elastollan® 1185 A WM | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| LNP™ THERMOCOMP™ JF004E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| Durethan® BKV 30 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |