Durethan® BKV 30 G H2.0 900051
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B3kRue_Durethan-BKV-30-G-H2-0-900051.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, improved resistance to weathering |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.58 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.16 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.27 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.060 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 230 | 140 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 9910 | 7090 | MPa | ASTM D638 |
| 23°C | 10000 | 6200 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Break, 23°C | 175 | 117 | MPa | ASTM D638 |
| Break, 23°C | 180 | 110 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | 6.0 | % | ASTM D638 |
| Break, 23°C | 3.0 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 9120 | 6820 | MPa | ASTM D790 |
| 23°C 5 | 9300 | 5700 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 276 | 200 | MPa | ASTM D790 |
| 3.5% Strain 6 | -- | 145 | MPa | ISO 178/A |
| 23°C 7 | 270 | 170 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 8(23°C) | 4.0 | 6.2 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-100, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 10 | 2.20 | -- | J | |
| -- 11 | 2.60 | -- | J | |
| Film Puncture Force | ISO 6603-2 | |||
| -- 12 | 735 | -- | N | |
| -- 13 | 838 | -- | N |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | 10 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 75 | 75 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 55 | 55 | kJ/m² | |
| 23°C | 65 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 14 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | 31 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.30 | 7.00 | ||
| 23°C, 1 MHz | 4.00 | 4.30 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 8.0E-3 | 0.13 | ||
| 23°C, 1 MHz | 0.017 | 0.050 | ||
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 475 | -- | V | |
| Solution B | 225 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 600 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 15 | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Pull Rate: 2 mm/min; 50% RH |
| 9 . | US-FMVSS302 |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | -30°C |
| 13 . | 23°C |
| 14 . | 10°C/min |
| 15 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® EC (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Asiga® PlasPINK | Asiga | Unspecified | Asiga® |
| Kumho PS HI 425EH | Korea Kumho Petrochemical Co., Ltd. | PS (HIPS) | Kumho PS |
| LNP™ THERMOCOMP™ ZF006 compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |
| Hostacom PPU X9057HS C11354 | LyondellBasell Industries | PP Copolymer | Hostacom |