Adflex Q 402 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B34bWO_Adflex-Q-402-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adflex Q 402 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is designed for air quenched blown film applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.65 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 49 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, 23°C | 15.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 21.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 27 | % | ISO 527-2 |
| Fracture, 23°C | > 800 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 480 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Resistance (50 µm) | 13.2 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| MD : 50 µm, blown film | 330 | MPa | ASTM D882 |
| TD : 50 µm, blown film | 300 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 18.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 15.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 68.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 48.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 670 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 870 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 550 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 50 µm, blown film | 0.045 | N | ISO 6383-2 |
| TD : 50 µm, blown film | 0.094 | N | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 57.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 108 | °C | ISO 306/A50 |
| Melting Temperature | 164 | °C | DSC |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Resistance | 152 | °C | Internal method |
| Film property values shown were determined on 50 µm (2.0 mil) thickness blown film extruded at 238°C (460°F), 2.5:1 BUR, with a 2 mm (80 mil) die gap. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 106955 | RTP Company | PP, Unspecified | RTP |
| Boda BDF401P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Clear Cote™ Crystal Clear Table Top Epoxy | Club Kit, Inc. | Epoxy | Clear Cote™ |
| E-FLEX™ I3265 | Mando Advanced Materials Co., Ltd. | EAA | E-FLEX™ |
| LNP™ LUBRICOMP™ CBL36XXC compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ LUBRICOMP™ |