Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ UL002S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B27S22_LNP-LUBRICOMP-UL002S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UL002S is a compound based on Polypthalamide resin containing 10% PTFE. Added features of this grade include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound UL-4020 HS Product reorder name: UL002S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 2.0 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.47 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.73 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3170 | MPa | ASTM D638 |
| -- | 3220 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Break 3 | 60.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.2 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 2.2 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 6(50.0 mm Span) | 2980 | MPa | ASTM D790 |
| Flexural Strength 7 | ASTM D790 | ||
| Yield, 50.0 mm Span | 105 | MPa | |
| Break, 50.0 mm Span | 105 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.27 | ||
| vs. Itself - Static | 0.17 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.100 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 20.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 26 | J/m | ASTM D256 |
| 23°C 8 | 2.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 9 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 2.80 | J | ASTM D3763 |
| -- | 0.500 | J | ISO 6603-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 149 to 171 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5165-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TF8CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| C-Clear™ K8262 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | C-Clear™ |
| Karina CLEAR PVC COMPOUND 45/203-DA-ATB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 2982-82 Clear 8463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |