DENIFORM 1010
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Vamp Tech |
| Trademark: | DENIFORM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B1zDAs_DENIFORM-1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM, 10% glass fiber reinforced, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.6 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 160 | °C | ASTM D1525 1 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Random Copolymer RP700 | M. Holland Company | PP Random Copolymer | MTEGRITY™ PP Random Copolymer |
| Aaron AVPP C 200-2 | Aaron Industries Corp. | PP Copolymer | Aaron |
| Chemlon® 66M8 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Karina WHITE PVC COMPOUND -E 753D10/ 11-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polygen SG6C-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |