Panlite® AM-9730Z
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B1niGt_Panlite-AM-9730Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate/Polyester alloy |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.70 to 1.0 | % | |
| Flow : 4.00 mm | 0.70 to 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 55.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 8.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 4-98 DF | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Zhongfa PC G2820 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC | Zhongfa |
| FERREX® GPP30CN33HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| Mafill® CR XG 3344 | Ravago Group | PP, Unspecified | Mafill® |
| Axiall PVC 7255 | Axiall Corporation | PVC, Rigid | Axiall PVC |