Order Products : sales@su-jiao.com
VAMPAMID 66 2526 V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B1iK0u_VAMPAMID-66-2526-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0 at 0,8 mm, 25% glass fiber reinforced, very good mechanical properties, CTI 400 V. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.90 | % | |
| Water Absorption (Saturation) | 0.70 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 240 | °C | ASTM D648A |
| Vicat Softening Temperature | 230 | °C | ASTM D1525 1 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 100 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PP 1351 | Premix Oy | TPO | PRE-ELEC® |
| RTP 3583 | RTP Company | FEP | RTP |
| AMPAL® MPV 2500 | RASCHIG GmbH | Polyester, TS | AMPAL® |
| Daplen™ ED223AE | Borealis AG | PP, Unspecified | Daplen™ |
| Geon™ Fiberloc™ 83520 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |